| Color: |
WHITE |
Type: |
4 |
|
Application
|
|
|
| Physical Properties: |
Composition Weight % |
| VHN After Firing: |
275 |
Au: |
0 |
| VHN Soft: |
--- |
Pt: |
0 |
| VHN Hard: |
--- |
Pd: |
53.965 |
| |
.
|
Ag: |
37.06 |
| Proof Stress Soft MPa: |
552 |
Cu: |
0
|
| Proof Stress Hard MPa: |
--- |
Zn: |
0
|
| |
|
Sn: |
8.5
|
| Tensile Strength Soft MPa: |
724 |
In: |
X
|
| Tensile Strength Hard MPa: |
--- |
Ga: |
0
|
| |
|
|
Other Pt Group Metals:
|
|
Ru(x)
|
|
| Elongation Soft: |
18 |
| Elongation Hard: |
--- |
Au and Pt Group: |
54 |
| Elastic Modulus GPa: |
137 |
Other Metal: |
Li(x) |
| |
|
PreSolder: |
HFWC |
| Melting Range C: |
1180-1280 |
PostSolder: |
LO |
| Casting Temp C: |
1345 |
|
Investment:
|
|
Phosphate Bonded
|
|
| Density g/cc: |
11 |
| Expansion at 500C: |
14.9 |
Crucible: Graphite / Ceramic |
| Expansion at 600C: |
15.1 |
|
Oxidation Procedure:
|
|
650-1040°C,
hold 10 min, Removal of oxide optional, no vacuum
|
|
| Burnout Temp C: |
815 |
| Laser Wire |
|
|
|